Volkswagen Touran Service Manual: Two-Part Brilliant Clear Coat
| Two-Part Brilliant Clear Coat -L2K 769 K04 A5- |
| Two-part HS brilliant clear coat is a high-gloss, VOC
compliant high solid clear coat from the two-part acrylic
system. |
| Very high stability under load |
| Very good gloss and depth |
| Can be used in a number of ways by adding thinner |
| Processing in two spray applications |
| Suitable preliminary coatings: |
|
|
|
| Two-Part VHS Hardener -LHA 009 051 A2-/-LVM 009 051 A5- |
| Two-Part VHS Hardener, Short -LHA 009 050 A2- |
| Two-Part VHS Hardener, Long -LHA 009 052 A2-/-LHA 009 052
A3- |
| Two-Part VHS Hardener, Extra Long -LHA 009 053 A2- |
| The choice of hardener depends on the temperature and the
size of the surface. See technical application information
two-part VHS hardener. Refer to
→ Chapter "Two-Part VHS Hardener and Two-Part VHS Performance
Hardener". |
| For elastification
→ Anchor. |
| Two-Part Thinner, Special -LVM 009 200 A2/A5- |
|
|
|
| Processing time/pot life: |
| |
Ready for spraying 60-75 minutes at +20 C (68 F). |
|
|
|
| |
Processing viscosity 4 mm for +20 C (68 F), German
Industry Standardization 53211 |
|
|
|
| Adding 10 % thinner at +20 C (68 F) material temperature. |
| |
Use a measuring stick to mix when pouring in the thinner. |
| Processing viscosity 4 mm gravity feed spraygun "Compliant"
and "HVLP": |
|
|
|
| DIN 4 mm: 18 to 21 seconds |
|
|
|
| |
Set spray nozzle (see manufacturer's information):
"Compliant" 1.2 to 1.3 mm. |
| |
Set spray nozzle (see manufacturer's information): "HVLP"
1.2 to 1.3 mm. |
| |
Set spray pressure (see manufacturer's information):
"Compliant" to 2.0 to 2.5 bar. |
| |
Set atomizing pressure (see manufacturer's information):
"HVLP" 0.7 bar. |
| |
Apply in two spray applications with a 5 to 10 minute
intermediate ventilation time. The first spray application is
applied lightly, but completely. |
| |
The recommended dry layer thickness is between 50 and 70 mm. |
|
|
|
| Final drying time with forced drying is at least 10 minutes. |
|
|
|
| Forced drying is at between +60 and 65 C (140 and 149 F)
for 35 to 40 minutes. |
|
|
|
| Final drying time for IR drying is a minimum of 5 to 10
minutes. |
|
|
|
| IR dry with a short-wave heater for 15 to 20 minutes and
with a medium-wave heater for 10 to 15 minutes |
|
|
|
| Elastification for rigid and semi-rigid plastics: |
| The base material must first be mixed with 15 % Elastic
Additive -ALZ 011 001-. |
| Mixture with two-part VHS hardeners, 3:1 with 10 % Two-Part
Thinner, Special -LVM 009 200 A2/A5- (drying period is
lengthened). |
|
|
|
| Delivery Viscosity |
DIN 4 mm, +20 C (68 F): 24
to 28 seconds |
| Flashpoint: |
above +23 C (73.4 F) |
| VOC value: 2004/42/IIB(d)(420)420 |
The EU limit for this product
(product category IIB.b) in ready-to-use form is a maximum of 420 g/L
volatile organic compounds. The VOC-value of this product in
ready-to-use form is a maximum of 420 g/L. |
| The guaranteed shelf life of Two-Part Brilliant Clear Coat
-L2K 769 K04 A5- is 48 months from date of manufacture. Use no
later than the date indicated on the label and store in original
container at +20 C (68 F). |
|
|
|
Definition:
Two-Part HS Optimum Plus Clear Coat -LZK 769 K07 A5-
Edition 04/2013
Product Description
...
Definition:
Two-Part HS Brilliant Plus Clear Coat -LZK 769 K05 A5-
Edition 02/2012
Product Description
...