Volkswagen Touran Service Manual: Two-Part HS Mixed Filler

Definition:
Two-Part HS Mixed Filler -LGF 810 150 A4-, white
Two-Part HS Mixed Filler -LGF 810 151 A4-, black
Two-Part HS Mixed Filler -LGF 810 152 A4-, red
Two-Part HS Mixed Filler -LGF 810 153 A2-, yellow
Two-Part HS Mixed Filler -LGF 810 154 A2-, blue
Two-Part HS Mixed Filler -LGF 810 155 A2-, green
Edition 04/2013
Product Description
The two-part HS mixed filler system is part of the latest generation of innovative color two-part acrylic-resin-based HS filler systems.
The system consists of 6 colored fillers (white, black, yellow, red, green, blue). These fillers can also be mixed together with the aid of simple formulas.
All settings of this product are VOC compliant.
Properties:
1 -  can be used as an interior color and as a "wet-in-wet" filler
Excellent, simple and variable processing options
Flows well
Very quick drying performance
Very nice paint finish
Great stability under load
High yield
2 -  can be used as sanding filler
sands well
Excellent high-build characteristics
Very good drying properties
‎Long curing time
Application Instructions
Base Surface
Suitable base surfaces:
sheet steel that has been cleaned, sanded and primed with Two-Part Wash Primer -LHV 043 000 A2- or One-Part Wash Primer -LVM 044 007/171 A2-, galvanized/electrolytically zinced sheet steel or soft aluminum
Fine or non-sanded, thoroughly cleaned, original factory primer.
Sanded factory paint or old paint (except TPA)
Surfaces prepared with two-part polyester products and then sanded very fine.
Cleaned and sanded UP-GF surfaces, free of separating agents
   
Pre-treatment of base surfaces:
  Carefully clean using Silicone Remover -LVM 020 000 A5- or Silicone Remover, Long -LVM 020 100 A5-.
  Two-Part HS Mixed Filler
  Then, sand.
  Two-Part HS Mixed Filler
  Use a suitable cleaning agent before reworking to ensure a clean and residue-free surface.
  Two-Part HS Mixed Filler
Use as interior color.
Mixture ratio:
  2:1 by volume with:
Two-Part HS Hardener -LHA 009 041 A3-
Two-Part HS Hardener, Short -LHA 021 004 A3-
Two-Part HS Hardener, Extra Short -LHA 009 046 A2-
Two-Part HS Hardener, Long -LHA 009 047 A3-
Two-Part HS Hardener, Extra Long -LHA 009 048 A3-
Two-Part HS Hardener, Special -LHA 009 049 A3-
  Two-Part HS Mixed Filler
Mixture ratio:
  3:1 by volume with:
Two-Part VHS Hardener, Short -LHA 009 050 A2-
Two-Part VHS Hardener -LHA 009 051 A2-/-LVM 009 051 A5-
Two-Part VHS Hardener, Long -LHA 009 052 A2-/-LHA 009 052 A3-
Two-Part VHS Hardener, Extra Long -LHA 009 053 A2-
Processing time/pot life:
  Ready to spray 50 to 60 minutes at +20 C (68 F) (depending on the hardener used)
Additive:
Mixed Filler Additive -LZS 811 000 A2-
  Two-Part HS Mixed Filler
Application type "coat"
  Two-Part HS Mixed Filler
  Processing viscosity 4 mm for +20 C, (68 F) German Industry Standardization 53211
Processing viscosity 4 mm gravity feed spraygun "Compliant" and "HVLP" 16 to 19 seconds
  Two-Part HS Mixed Filler
Adding 20 % HS hardener and 40 % VHS hardener at +20 C (68 F) material temperature
  Use a measuring stick to mix when pouring in the hardener.
  Two-Part HS Mixed Filler
  Set spray nozzle (see manufacturer's information): "Compliant" 1.2 to 1.4 mm.
  Set spray nozzle (see manufacturer's information): "HVLP" 1.3 to 1.5 mm.
  Set spray pressure (see manufacturer's information): "Compliant" to 1.5 to 3.0 bar.
  Set atomizing pressure (see manufacturer's information): "HVLP" 0.7 bar.
  Two-Part HS Mixed Filler
  Three spray applications are required to get a dry layer thickness of between 30 and 70 mm.
More coats may be required, depending upon the color.
  Note
When using as an interior color, overpainting the top coats does not apply.
  Two-Part HS Mixed Filler
Use as "wet-in-wet" filler
Mixture ratio:
  2:1 by volume with:
Two-Part HS Hardener -LHA 009 041 A3-
Two-Part HS Hardener, Short -LHA 021 004 A3-
Two-Part HS Hardener, Long -LHA 009 047 A3-
Two-Part HS Hardener, Extra Long -LHA 009 048 A3-
  Two-Part HS Mixed Filler
Mixture ratio:
  3:1 by volume with:
Two-Part VHS Hardener -LHA 009 051 A2-/-LVM 009 051 A5-
Two-Part VHS Hardener, Long -LHA 009 052 A2-/-LHA 009 052 A3-
Two-Part VHS Hardener, Extra Long -LHA 009 053 A2-
For elastification. Refer to → Anchor.
  Two-Part HS Mixed Filler
Processing time/pot life:
  Ready to spray for 60 minutes at +20 C (68 F) (depending on the hardener used)
Additive:
Mixed Filler Additive -LZS 811 000 A2-
  Two-Part HS Mixed Filler
Application type "coat"
  Two-Part HS Mixed Filler
  Processing viscosity 4 mm for +20 C (68 F), German Industry Standardization 53211
Processing viscosity 4 mm gravity feed spraygun "Compliant" and "HVLP" 16 to 19 seconds
  Two-Part HS Mixed Filler
Adding 20 to 30 % HS hardener and 40 to 50 % VHS hardener at +20 C (68 F) material temperature
  Use a measuring stick to mix when pouring in the hardener.
  Two-Part HS Mixed Filler
  Set spray nozzle (see manufacturer's information): "Compliant" 1.2 to 1.4 mm.
  Set spray nozzle (see manufacturer's information): "HVLP" 1.3 to 1.5 mm.
  Set spray pressure (see manufacturer's information): "Compliant" to 2.0 to 2.5 bar.
  Set atomizing pressure (see manufacturer's information): "HVLP" 0.7 bar.
  Two-Part HS Mixed Filler
  One to two spray applications are required to get a dry layer thickness of 30 mm.
  Two-Part HS Mixed Filler
Drying time for "wet-in-wet" processing at +20 C (68 F) room temperature before applying the top coat:
with water-based base paint for 30 to 120 minutes
with two-part HS top coat for 15 to 120 minutes
  Two-Part HS Mixed Filler
Fast Point Repair System
Drying time for "wet-in-wet" processing at +20 C (68 F) room temperature before applying the top coat:
with Two-Part HS Hardener, Extra Short -LHA 009 046 A2- for 15 minutes
with Two-Part VHS Hardener, Short -LHA 009 050 A2- for 15 minutes
  Two-Part HS Mixed Filler
Adding Mixed Filler Additive -LZS 811 000 A2- 20 to 30 % HS hardener and 40 to 50 % VHS hardener at +20 C (68 F) material temperature.
  Use a measuring stick to mix when pouring in the additive.
  Two-Part HS Mixed Filler
Adding thinner 10 % Two-Part Thinner, Plus -LHA 014 000 A5- at +20 C (68 F) material temperature.
  Use a measuring stick to mix when pouring in the thinner.
  Two-Part HS Mixed Filler
Reworking
Can be painted over with:
Water-based base paint and two-part HS clear coat
Two-Part HS Top Coat
  Two-Part HS Mixed Filler
Use as Sanding Filler
Mixture ratio:
  4:1 by volume with:
Two-Part HS Hardener -LHA 009 041 A3-
Two-Part HS Hardener, Short -LHA 021 004 A3-
Two-Part HS Hardener, Extra Short -LHA 009 046 A2-
Two-Part HS Hardener, Long -LHA 009 047 A3-
Two-Part HS Hardener, Extra Long -LHA 009 048 A3-
  Two-Part HS Mixed Filler
Mixture ratio:
  7:1 by volume with:
Two-Part VHS Hardener, Short -LHA 009 050 A2-
Two-Part VHS Hardener -LHA 009 051 A2-/-LVM 009 051 A5-
Two-Part VHS Hardener, Long -LHA 009 052 A2-/-LHA 009 052 A3-
Two-Part VHS Hardener, Extra Long -LHA 009 053 A2-
For elastification. Refer to → Anchor.
  Two-Part HS Mixed Filler
Processing time/pot life:
  Ready to spray 90 to 120 minutes at +20 C (68 F) (depending on the hardener used).
Thinner:
Two-Part Thinner -LVE 009 001 A5-
Two-Part Thinner, Long -LVM 009 300 A2-
Two-Part Thinner, Plus -LHA 014 000 A5-
Two-Part Thinner, Special -LVM 009 200 A2/A5-
  Two-Part HS Mixed Filler
Application type "coat"
  Two-Part HS Mixed Filler
  Processing viscosity 4 mm for +20 C, (68 F) German Industry Standardization 53211
Processing viscosity 4 mm gravity feed spraygun "Compliant" and "HVLP" 18 to 20 seconds
  Two-Part HS Mixed Filler
Adding 15 % HS hardener and 25 % VHS hardener at +20 C (68 F) material temperature.
  Use a measuring stick to mix when pouring in the hardener.
  Two-Part HS Mixed Filler
  Set spray nozzle (see manufacturer's information): "Compliant" 1.3 to 1.7 mm.
  Set spray nozzle (see manufacturer's information): "HVLP" 1.3 to 1.5 mm.
  Set spray pressure (see manufacturer's information): "Compliant" to 2.0 to 2.5 bar.
  Set atomizing pressure (see manufacturer's information): "HVLP" 0.7 bar.
  Two-Part HS Mixed Filler
  Two to four spray applications are required (depending on spray nozzle used) to get a dry layer thickness of 200 mm.
When air drying, the maximum dry layer thickness is 200 mm.
When forced drying, the maximum dry layer thickness is 150 mm.
When IR drying (bright colors), the maximum dry layer thickness is 150 mm.
When IR drying (dark colors), the maximum dry layer thickness is 120 mm.
  Two-Part HS Mixed Filler
Drying
The material can be sanded after 3 to 4 hours (layer thickness of 60 to 150 mm after air drying at +20 C (68 F) room temperature).
If the applied layer thickness is between 150 and 200 mm, the material should be allowed to dry over night and then sanded.
  Two-Part HS Mixed Filler
Final drying time with forced drying is a minimum of 5 to 15 minutes.
  Two-Part HS Mixed Filler
Forced drying at +60 C (140 F) object temperature for 30 to 35 minutes to 60 to 150 mm
  Two-Part HS Mixed Filler
Final drying time for IR drying is a minimum of 5 to 10 minutes.
  Two-Part HS Mixed Filler
When IR drying (depending on layer thickness), use the medium-wave radiator for 15 minutes and the short-wave radiator for 10 minutes (of these, dry for 2 minutes at 50 % power and 8 minutes at 100 % power)
  P00-10028
Further Processing
  Dry-sand with rotary sander and dust extraction. P400-500 grit sandpaper
  Two-Part HS Mixed Filler
  Wet-sand with P800-1000 grit sandpaper
  Two-Part HS Mixed Filler
Reworking
Can be painted over with:
Water-based base paint and two-part HS clear coat
Two-Part HS Top Coat
  Two-Part HS Mixed Filler
Special Instructions
Elastification for rigid and semi-rigid plastics:
The base material must first be mixed with 15 % Elastic Additive -ALZ 011 001-.
When engaged in "wet-in-wet" processing, use 2:1 two-part HS hardener and 30 % Mixed Filler Additive -LZS 811 000 A2-
When engaged in "wet-in-wet" processing, use 3:1 two-part VHS hardener and 40 % Mixed Filler Additive -LZS 811 000 A2-
When processing "as sanding filler", use 3:1 two-part HS hardener and 10 % thinner
When processing "as sanding filler", use 4:1 two-part VHS hardener and 20 % thinner
  Two-Part HS Mixed Filler
Before applying the water-based base paint, allow for 45 minutes of ventilation time at +20 C (68 F) room temperature.
  Two-Part HS Mixed Filler
When using "sanding filler", the oven drying time is 45 minutes.
Any faults in the base surface can be filled with two-part polyester filling paste. After drying and intermediate sanding, insulate the filler patches with two-part HS mixed filler.
The best insulating effect, even with critical surfaces, is achieved with a medium layer of 60 to 120 mm in 2 spray passes, with air-drying overnight, or oven/IR drying. With critical surfaces, fine preparation is required and the parts must be evenly filled.
The Two-Part HS Vario Filler -LGF 786 004 A4- (gray) is recommended for insulating thermoplastic coatings.
When air drying, maintaining a minimum temperature of +8 to 15 C (59 F) while using Two-Part HS Hardener, Extra Short -LHA 009 046 A2- is recommended.
  Two-Part HS Mixed Filler
Personal Protective Equipment:
Note the safety data sheets
Wear the personal protective equipment during application
Characteristics
  Two-Part HS Mixed Filler
Delivery Viscosity Thixotropic
Flashpoint: above 23 C (73.4F)
VOC value: 2004/42/IIB(c)(540)540 The EU limit for this product (product category IIB.b) in ready-to-use form is a maximum of 540 g/L volatile organic compounds. The VOC value of this product in ready-to-use form is a maximum of 540 g/L.
 
     
Storage
The guaranteed shelf life of 24 months (48 months for mixed filler additive) from date of manufacture. Use no later than the date indicated on the label and store in original container at +20 C (68 F).
  Two-Part HS Mixed Filler
Two-Part HS Premium Filler
Definition: Two-Part HS Premium Filler -LVM 013 171 A4-, dark gray Two-Part HS Premium Filler -LGF 013 007 A4-, light gr ...

Two-Part HS Performance Filler
Definition: Two-Part HS Performance Filler -LVM 014 100 A4-, white Two-Part HS Performance Filler -LVM 014 173 A4-, dark ...

Other materials:

Unlocking the tailgate manually
Fig. 194 Inside the luggage compartment: unlocking the tailgate manually First read and observe the introductory information and safety warnings  If necessary, fold back the backrest of the third row of seats   . If necessary, remove items of luggage so you can reach the tailgate ...

Introduction
This chapter contains information on the following subjects:  → How to start the engine using jump leads   If the engine cannot be started because of a discharged vehicle battery, the battery can be connected to the battery of another vehicle to start the engine. Before using jump le ...

Vehicle identification data
Fig. 15 A: Vehicle data sticker: example shows a vehicle with engine code CBFA ③ B: Type plate Fig. 16 Vehicle identification number First read and observe the introductory information and safety warnings Vehicle identification number The vehicle identification number can be r ...

© 2016-2018 Copyright www.vwtouran.net