Volkswagen Touran Service Manual: Two-Part HS Wet-in-Wet Filler

Definition:
Two-Part HS Wet-in-Wet Filler -LVM 013 008 A4-, light gray
Two-Part HS Wet-in-Wet Filler -LVM 013 905 A4-, black
Edition 03/2015
Product Description
The two-part HS wet-in-wet filler (light gray) is a high-quality, VOC compliant, two-part HS wet-in-wet acrylic resin-based filler.
Properties:
Excellent processing properties
Long pot life
Flows well
Quick processing and reworking
For economical application in wet-in-wet processes, especially use with water-based paint.
Very good stability under load
Application Instructions
Base Surface
Suitable base surfaces:
sheet steel that has been cleaned, sanded and primed with Two-Part Wash Primer -LHV 043 000 A2- or One-Part Wash Primer -LVM 044 007/171 A2-, galvanized/electrolytically zinced sheet steel or soft aluminum
Fine or non-sanded, thoroughly cleaned, original factory primer.
Thoroughly sanded factory paint or old paint
Surfaces prepared with two-part polyester products and then sanded very fine.
Cleaned and sanded UP-GF surfaces, free of separating agents
   
Pre-treatment of base surfaces:
  Carefully clean using Silicone Remover -LVM 020 000 A5- or Silicone Remover, Long -LVM 020 100 A5-.
  Two-Part HS Wet-in-Wet Filler
  Then, sand.
  Two-Part HS Wet-in-Wet Filler
  Use a suitable cleaning agent before reworking to ensure a clean and residue-free surface.
  Two-Part HS Wet-in-Wet Filler
Wet-in-wet process
Mixture ratio:
  5:1 by volume with:
Two-Part VHS Hardener -LHA 009 051 A2-/-LVM 009 051 A5-
Two-Part VHS Hardener, Long -LHA 009 052 A2-/-LHA 009 052 A3-
Two-Part VHS Hardener, Extra Long -LHA 009 053 A2-
  Two-Part HS Wet-in-Wet Filler
Mixture ratio:
  3:1 by volume with:
Two-Part HS Hardener, Short -LHA 021 004 A3-
Two-Part HS Hardener -LHA 009 041 A3-
Two-Part HS Hardener, Long -LHA 009 047 A3-
Two-Part HS Hardener, Extra Long -LHA 009 048 A3-
For Elastification. Refer to → Anchor.
  Two-Part HS Wet-in-Wet Filler
Processing time/pot life:
  Ready to spray 90 to 120 minutes at +20 C (68 F) (depending on the hardener used).
Thinner:
Two-Part Thinner -LVE 009 001 A5-
Two-Part Thinner, Special -LVM 009 200 A2/A5-
  Two-Part HS Wet-in-Wet Filler
Application type "coat"
  Two-Part HS Wet-in-Wet Filler
  Processing viscosity 4 mm for +20 C (68 F), German Industry Standardization 53211
  Two-Part HS Wet-in-Wet Filler
Processing viscosity 4 mm gravity feed spraygun "Compliant" and "HVLP" is the mixed viscosity.
  Use a measuring stick to mix when pouring in the hardener.
  Two-Part HS Wet-in-Wet Filler
  Set spray nozzle (see manufacturer's information): "Compliant" 1.3 to 1.4 mm.
  Set spray nozzle (see manufacturer's information): "HVLP" 1.3 to 1.4 mm.
  Set spray pressure (see manufacturer's information): "Compliant" to 1.5 to 2.0 bar.
  Set atomizing pressure (see manufacturer's information): "HVLP" 0.7 bar.
  Two-Part HS Wet-in-Wet Filler
  1 to 2 spray applications are required to get the recommended dry layer thickness of 25 to 30 mm.
  Two-Part HS Wet-in-Wet Filler
The drying time before continuing work is 15-20 minutes at +20 C (68 F)room temperature (maximum 8 hours before applying the top coat).
  Two-Part HS Wet-in-Wet Filler
Reworking
Can be painted over with:
Water-based base paint and two-part HS clear coat
Two-Part HS Top Coat
Special Instructions
Elastification for rigid and semi-rigid plastics:
The base material must first be mixed with 15 % Two-Part Elastic Additive -ALZ 011 001-. 3:1 mixture ratio for VHS hardeners with 20% thinner, 2:1 mixture ratio for HS hardeners with 20 % thinner.
  Note
The drying time before applying the base paint or two-part top coat increases to 30 to 45 minutes.
  Two-Part HS Wet-in-Wet Filler
Personal Protective Equipment:
Note the safety data sheets
Wear the personal protective equipment during application
Characteristics
  Two-Part HS Wet-in-Wet Filler
Flashpoint: above +23 C (73.4 F)
VOC value: 2004/42/IIB(c)(540)540 The EU limit for this product (product category IIB.b) in ready-to-use form is a maximum of 540 g/L volatile organic compounds. The VOC value of this product in ready-to-use form is a maximum of 540 g/L.
 
     
Storage
The guaranteed shelf life is 24 months from production date. Use no later than the date indicated on the label and store in original container at +20 C (68 F).
  Two-Part HS Wet-in-Wet Filler
Two-Part Synthetic Adhesion Filler
Definition: Two-Part Synthetic Adhesion Filler -LKF 696 009 A2-, white Two-Part Synthetic Adhesion Filler -LKF 696 040 A ...

Top Coats
...

Other materials:

Aquaplus Touch-Up Additive
Definition: t  Touch-Up Additive for Aquaplus -LVM 030 000 A2-   Note The usage and application instructions for the Touch-Up Additive for Aquaplus -LVM 030 000 A2- is described here →&n ...

Two-Part HS Performance Filler
Definition: Two-Part HS Performance Filler -LVM 014 100 A4-, white Two-Part HS Performance Filler -LVM 014 173 A4-, dark gray Two-Part HS Performance Filler -LVM 014 190 A4-, anthracite ...

Tires, Storing
Storage Room Tire storage must be: Dark, Dry, Cool and Ventilated     ...

© 2016-2018 Copyright www.vwtouran.net