Volkswagen Touran Service Manual: Two-Part HS Optimum Clear Coat
| Two-Part HS Optimum Clear Coat -LZK 769 K02 A5- |
| Two-part HS optimum clear coat is a VOC compliant (VOC value
less than 420 g/L), high-quality and productive high solid clear
coat. |
| Easy and economical processing |
| Very good spreading properties |
| Suitable preliminary coatings: |
|
|
|
| Two-Part VHS Hardener -LHA 009 051 A2-/-LVM 009 051 A5- |
| Two-Part VHS Hardener, Short -LHA 009 050 A2- |
| Two-Part VHS Hardener, Long -LHA 009 052 A2-/-LHA 009 052
A3- |
| Two-Part VHS Hardener, Extra Long -LHA 009 053 A2- |
| See technical application information for the two-part VHS
hardener. Refer to
→ Chapter "Two-Part VHS Hardener and Two-Part VHS Performance
Hardener". |
| For elastification
→ Anchor. |
|
|
|
| Processing time/pot life: |
| |
Ready to spray in 80-100 minutes at +20 C (68 F) |
|
|
|
| |
Processing viscosity at +20 C (68 F) material temperature
is the mixing viscosity for "Compliant" and "HVLP". |
|
|
|
| |
Set spray nozzle (see manufacturer's information):
"Compliant" 1.2 to 1.3 mm. |
| |
Set spray nozzle (see manufacturer's information): "HVLP"
1.3 to 1.4 mm. |
| |
Set spray pressure (see manufacturer's information):
"Compliant" to 2.0 to 2.5 bar. |
| |
Set atomizing pressure (see manufacturer's information):
"HVLP" 0.7 bar. |
|
|
|
 Note
| During the spray application process, the first half spray
application should form a thin, nearly complete film upon which
a fully-completed spray application can be applied. |
| |
The recommended dry layer thickness is between 45 and 55 mm. |
|
|
|
| Air dry at +20 C (68 F) room temperature: |
| Dust dry after 40 to 50 minutes |
| Ready for assembly after 4 to 6 hours |
|
|
|
| Final drying time with forced drying is a minimum of 5 to 10
minutes. |
|
|
|
| Forced drying at +60 C (140 F) object temperature with: |
| Two-Part VHS Hardener -LHA 009 051 A2-/-LVM 009 051 A5- for
20 to 25 minutes. |
| Two-Part VHS Hardener, Short -LHA 009 050 A2- for 15 to 20
minutes. |
| Two-Part VHS Hardener, Long -LHA 009 052 A2-/-LHA 009 052
A3- for 20 to 30 minutes. |
| Two-Part VHS Hardener, Extra Long -LHA 009 053 A2- for 25 to
35 minutes. |
|
|
|
| Final drying time for IR drying is a minimum of 5 to 10
minutes. |
|
|
|
| IR dry with short-wave heater for 8 to 12 minutes |
|
|
|
| Elastification for rigid and semi-rigid plastics: |
| The base material must first be mixed with 15 % Elastic
Additive -ALZ 011 001-. |
| Mixing two-part VHS hardeners, 3:1 with 5 % thinner (drying
extends this). |
|
|
|
| Personal Protective Equipment: |
| Note the safety data sheets |
| Wear the personal protective equipment during application |
|
|
|
| Flashpoint: |
above +23 C (73.4 F) |
| VOC value: 2004/42/IIB(d)(420)420 |
The EU limit for this product
(product category IIB.b) in ready-to-use form is a maximum of 420 g/L
volatile organic compounds. The VOC-value of this product in
ready-to-use form is a maximum of 420 g/L. |
| The guaranteed shelf life of Two-Part HS Optimum Clear Coat
-LZK 769 K02 A5- is 48 months from date of manufacture. Use no
later than the date indicated on the label and store in original
container at +20 C (68 F). |
|
|
|
Definition:
Two-Part HS Vario Clear Coat -L2K 769 K01 A5-
Edition 06/2013
Product Description
...
Definition:
Two-Part HS Optimum Plus Clear Coat -LZK 769 K07 A5-
Edition 04/2013
Product Description
...