Volkswagen Touran Service Manual: Two-Part HS Vario Clear Coat

Definition:
Two-Part HS Vario Clear Coat -L2K 769 K01 A5-
Edition 06/2013
Product Description
Two-part HS vario clear coat is a VOC compliant (VOC value less than 420 g/L), high-quality and productive high solid clear coat.
Properties:
Easy and quick to process
Variable uses for two-part HS and two-part VHS hardeners
Good spreading properties
Dries quickly
Easy to polish
Application Instructions
Base Surface
Suitable preliminary coatings:
Water-based base paints
   
Processing with Two-Part HS Hardeners
Mixture ratio:
  2:1 by volume with:
Two-Part HS Hardener -LHA 009 041 A3-
Two-Part HS Hardener, Short -LHA 021 004 A3-
Two-Part HS Hardener, Long -LHA 009 047 A3-
Two-Part HS Hardener, Extra Long -LHA 009 048 A3-
For Elastification. Refer to → Anchor.
  Two-Part HS Vario Clear Coat
Processing time/pot life:
  Ready to spray in 60 to 90 minutes at +20 C (68 F) (depending on the hardener used)
  Two-Part HS Vario Clear Coat
Application type "coat"
  Two-Part HS Vario Clear Coat
  Processing viscosity at +20 C (68 F) material temperature is the mixing viscosity for "Compliant" and "HVLP".
  Two-Part HS Vario Clear Coat
  Set spray nozzle (see manufacturer's information): "Compliant" 1.2 to 1.3 mm.
  Set spray nozzle (see manufacturer's information): "HVLP" 1.3 to 1.4 mm.
  Set spray pressure (see manufacturer's information): "Compliant" to 2.0 to 2.5 bar.
  Set atomizing pressure (see manufacturer's information): "HVLP" 0.7 bar.
  Two-Part HS Vario Clear Coat
  Apply 1.5 coats.
  Note
During the spray application process, the first half spray application should form a thin, nearly complete film upon which a fully-completed spray application can be applied.
  The recommended dry layer thickness is between 50 and 60 mm.
  Two-Part HS Vario Clear Coat
Processing with two-part VHS hardeners
Mixture ratio:
  3:1 by volume with:
Two-Part VHS Hardener -LHA 009 051 A2-/-LVM 009 051 A5-
Two-Part VHS Hardener, Short -LHA 009 050 A2-
Two-Part VHS Hardener, Long -LHA 009 052 A2-/-LHA 009 052 A3-
Two-Part VHS Hardener, Extra Long -LHA 009 053 A2-
See technical application information for the two-part VHS hardener. Refer to → Chapter "Two-Part VHS Hardener and Two-Part VHS Performance Hardener".
Thinner:
Two-Part Thinner, Special -LVM 009 200 A2-/-LVM 009 200 A5-
Two-Part Thinner, Long -LVM 009 300 A2-
HS Spot Thinner -LVM 006 000 A2-. Observe the technical application information. Refer to → Chapter "HS Spot Thinner".
For Elastification. Refer to → Anchor.
  Two-Part HS Vario Clear Coat
Processing time/pot life:
  Ready to spray in 60 to 90 minutes at +20 C (68 F) (depending on the hardener used)
  Two-Part HS Vario Clear Coat
Application type "coat"
  Two-Part HS Vario Clear Coat
  Processing viscosity at +20 C (68 F) material temperature is the mixing viscosity for "Compliant" and "HVLP".
  Two-Part HS Vario Clear Coat
  Add 12.5 % Two-Part Thinner, Special -LVM 009 200 A2-/-LVM 009 200 A5- /Two-Part Thinner, Long -LVM 009 300 A2- at + 20 C (68 F) material temperature.
  Two-Part HS Vario Clear Coat
  Set spray nozzle (see manufacturer's information): "Compliant" 1.2 to 1.3 mm.
  Set spray nozzle (see manufacturer's information): "HVLP" 1.3 to 1.4 mm.
  Set spray pressure (see manufacturer's information): "Compliant" to 2.0 to 2.5 bar.
  Set atomizing pressure (see manufacturer's information): "HVLP" 0.7 bar.
  Two-Part HS Vario Clear Coat
  Apply 1.5 coats.
  Note
During the spray application process, the first half spray application should form a thin, nearly complete film upon which a fully-completed spray application can be applied.
When using as a clear coat for minimal damage repairs (clever repair procedure), 12.4 % Two-Part Thinner, Special -LVM 009 200 A2- can be replaced with 12.5 % HS Spot Thinner -LVM 006 000 A2-. Do not apply on slanted surfaces.
  The recommended dry layer thickness is between 50 and 60 mm.
  Two-Part HS Vario Clear Coat
Drying
Air dry at +20 C (68 F) room temperature:
Dust dry after 20 to 30 minutes
Ready for assembly after 4 to 5 hours
Dry overnight
  Two-Part HS Vario Clear Coat
Final drying time with forced drying is a minimum of 5 to 10 minutes.
  Two-Part HS Vario Clear Coat
Forced dry at +60 C (140 F) object temperature for 20 to 30 minutes
  P00-10027
Final drying time for IR drying is at least 5 minutes.
  Two-Part HS Vario Clear Coat
IR dry with a short-wave heater for 10 to 15 minutes and with a medium-wave heater for 15 to 20 minutes
  Two-Part HS Vario Clear Coat
Special Instructions
Elastification for rigid and semi-rigid plastics:
The base material must first be mixed with 15 % Elastic Additive -ALZ 011 001-.
Mixture with two-part HS hardeners, 2:1
Mixing two-part VHS hardeners, 3:1 with 20 % thinner (drying extends this).
When using as a clear coat for minimal damage repairs (clever repair procedure), 12.5 % Two-Part Thinner, Special -LVM 009 200 A2-/-LVM 009 200 A5- can be replaced with 12.5 % HS Spot Thinner -LVM 006 000 A2-. Do not apply on slanted surfaces.
  Two-Part HS Vario Clear Coat
Personal Protective Equipment:
Note the safety data sheets
Wear the personal protective equipment during application
Characteristics
  Two-Part HS Vario Clear Coat
Flashpoint: above +23 C (73.4 F)
VOC value: 2004/42/IIB(d)(420)420 The EU limit for this product (product category IIB.b) in ready-to-use form is a maximum of 420 g/L volatile organic compounds. The VOC-value of this product in ready-to-use form is a maximum of 420 g/L.
 
     
Storage
The guaranteed shelf life of Two-Part HS Vario Clear Coat -L2K 769 K01 A5- is 48 months from date of manufacture. Use no later than the date indicated on the label and store in original container at +20 C (68 F).
  Two-Part HS Vario Clear Coat
Two-Part MS Matte Clear Coat
Definition: Two-Part MS Matt Clear Coat -L2K 769 020 A2- Edition 08/2013 Product Description ...

Two-Part HS Optimum Clear Coat
Definition: Two-Part HS Optimum Clear Coat -LZK 769 K02 A5- Edition 10/2012 Product Description ...

Other materials:

Various securing systems
Fig. 71 On the rear seats: figures Ⓐ and Ⓑ illustrate the main securing points for the child restraint system on the lower retaining rings and top tether. Figure Ⓒ shows how to secure the child restraint system using the vehicle's seat belt First read and observe the introd ...

Refrigerant in A/C Service station Container, Filling
  Caution If it is suspected that chemicals were added to the refrigerant circuit to seal leaks, do not connect the A/C service station and do not extract the refrigerant. ...

Frontal collisions and the laws of physics
Fig. 52 Passengers of a vehicle heading for a brick wall. They are not wearing seat belts Fig. 53 A vehicle with unbelted occupants strikes the wall First read and observe the introductory information and safety warnings The physical principles involved in a frontal collision are r ...

© 2016-2018 Copyright www.vwtouran.net